Презентация на тему Objective

ObjectiveThe aim of this study was to investigate the magnetic properties of hexaferrite powders SrFe12O19 strontium obtained by crystallization of the oxide glass, with the addition of Fe-B.                                                                                                       
Student: Vasilenko R.V.Group: MF-13-1Effect receiving modes, and heat treatment on the structure ObjectiveThe aim of this study was to investigate the magnetic properties of To achieve this aim the following tasks:Preparation of the alloy samples of СomminutionSAND planetary mill was used to prepare nanocrystalline powders of strontium hexaferrite The hysteresis loop of strontium hexaferrite and strontium hexaferrite with additions of iron boride. Oxide glass crystallization method obtained submicrocrystalline rapidly quenched alloys and amorphous structure.It Thank you for attention!
Слайды презентации

Слайд 2 Objective
The aim of this study was to investigate

ObjectiveThe aim of this study was to investigate the magnetic properties

the magnetic properties of hexaferrite powders SrFe12O19 strontium obtained

by crystallization of the oxide glass, with the addition of Fe-B.

                                                                                                       

Слайд 3 To achieve this aim the following tasks:

Preparation of

To achieve this aim the following tasks:Preparation of the alloy samples

the alloy samples of strontium hexaferrite composition of 95%

SrFe12O19 and 5% Fe-B.
Testing methods of heat treatment;
The study of the magnetic properties of the samples after grinding;

Tasks


Слайд 4 Сomminution
SAND planetary mill was used to prepare nanocrystalline

СomminutionSAND planetary mill was used to prepare nanocrystalline powders of strontium

powders of strontium hexaferrite with the ability to use

up to 4 sealable drums.

Measurements of the magnetic properties   Measurement of the hysteresis properties of the samples is carried out at room temperature for gisterezisgrafe using microwebermeter F192.

Pressing
Was conducted on "Hydraulic press" install at 60 kg / cm 2 (pre-powder in the mold magnetized in a magnetic field).

Experimental technique


Слайд 5

The hysteresis loop of strontium hexaferrite and strontium

The hysteresis loop of strontium hexaferrite and strontium hexaferrite with additions of iron boride.

hexaferrite with additions of iron boride.


Слайд 6
Oxide glass crystallization method obtained submicrocrystalline rapidly quenched

Oxide glass crystallization method obtained submicrocrystalline rapidly quenched alloys and amorphous

alloys and amorphous structure.
It is shown that vitrified grinding

in distilled water, compared to grinding in toluene resulted in a slight decrease in the coercive force (from 9 to kilooersted 8,2 kilooersted) and increase residual induction (from 0,75 kilogauss to 1,25 kilogauss, respectively.
After annealing at presszagotovki 1050 C at 30 min following magnetic properties obtained


Conclusions.